Bone regeneration around implants with modified surface by acid conditioning with the fluoride ions deposition

Published: 15 April 2020
Abstract Views: 590
pdf: 493
Publisher's note
All claims expressed in this article are solely those of the authors and do not necessarily represent those of their affiliated organizations, or those of the publisher, the editors and the reviewers. Any product that may be evaluated in this article or claim that may be made by its manufacturer is not guaranteed or endorsed by the publisher.

Authors

Aim Evaluate the late bone regeneration around implants with machined (MS) and acid modified surfaces followed by the deposition of fluoride ions (AFS) in the tibiae of rabbits.

Materials and methods Ti-cp disks and implants underwent the topographic characterization before surgery through scanning electron microscope, x-ray energy dispersive spectrometer (SEM-EDX), roughness average (Ra) and, cross section. Six rabbits received 12 implants in their tibiae. After 12 weeks, euthanasia was performed. The percentage of bone interface contact (BIC%) and neoformed bone area (NBA%) was measured. Data were submitted to the statistical analysis.

Results SEM-EDX revealed smooth surface, contaminated with machining residues and peaks of Ti for MS group and AFS group, peaks and valleys with presence of Ti, O, Na, Cl and F. Ra showed statistical difference between AFS (1.34 ± 0.35 µm) than MS (0.4 ± 0.06 µm). Cross section showed a mean thickness of 7.84 ± 3.73 μm for ASF and 1.26 ± 0.55 μm for MS. The mean values of BIC% for AFS were statistically higher than MS. For NBA% there is no statistical difference between grups.

Conclusions The surface modified by acid conditioning followed the addition of fluoride ions provides superior osseointegration process, even in the later periods of bone regeneration.

Dimensions

Altmetric

PlumX Metrics

Downloads

Download data is not yet available.

Citations

How to Cite

de Souza, A. S., Colombo, L. T., Hadad, H., Santos, A. F. P., Capalbo da Silva, R., Poli, P. P., Elias, C. N., Vedovatto, E., Souza, F. Á., & de Carvalho, P. S. P. (2020). Bone regeneration around implants with modified surface by acid conditioning with the fluoride ions deposition. Journal of Osseointegration, 12(3), 222–228. https://doi.org/10.23805/JO.2020.12.01.12